Delamination and spallation of thermal barrier coating (TBC) systems, used in hot parts of gas turbines, have been studied with respect to thermal fatigue. TBCs with and without pre-existing cracks were investigated. Thermal shock tests were performed until coating spallation. The experimental results revealed that the cracks primarily responsible for spallation grew horizontally, close to the int